Generalization of the Temperature Dependence of Some Physical Properties of High-strength Polyethylene (HDPE) Using the Method of Given Parameters

Received: 15 July 2019     Accepted: 19 August 2019     Published: 11 December 2019
Views:       Downloads:
Abstract

In this paper, based on the study of HDPE by dilatometric and rheological methods in a wide range of temperatures and cooling and deformation rates, we generalized the temperature dependence of the physical properties of polyethylene using the specified parameters method. Test specimens (cylinder size: height 12 mm, diameter 9.3 mm) were obtained both in the dilatometer’s test cylinder itself and in a specially designed injection mold using injection molding on a TP-125 injection molding machineThe temperatures in the experiments were added and maintained with an accuracy of 3.2.°C. Defined by The dependence of ρ_0 T_0 / ρT (relative reduced density of the polymer) on the reduced temperature (T - T0). Test specimens (cylinder size: height 12 mm, diameter 9.3 mm) were obtained both in the dilatometer’s test cylinder itself and in a specially designed injection mold using injection molding on a TP-125 injection molding machine. It was found that a reliable characteristic of the dilatometric properties of the crystallizing polymer, physically correctly and completely reflecting the features of the crystalline structure, can be obtained only in the mode of stepwise temperature changes, when at each given temperature the equilibrium value of the specific sample of the primer is fixedThus, the practical value of the dilatometric method for studying crystallizing polymers is shown, especially when comparing the results of dilatometry with the results of rheological studies.

Published in American Journal of Chemical Engineering (Volume 7, Issue 6)
DOI 10.11648/j.ajche.20190706.11
Page(s) 130-134
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2019. Published by Science Publishing Group

Keywords

Dilatometry, Viscosity, Rheology, Melt, High-strength Polyethylene (HDPE), Brittleness Temperature, Parameter

References
[1] Buniyat-zade A. A. Sagalaev G. V., Ismailov T. M., Svyatodukhov B. P. Plastics, 1972, 12, p. 44-46.
[2] Fisher. Chemistry and technology of polymers. 10, 119, 1965.
[3] Mandelykern L. Crystallization of polymers. Per. with English, ed. S. Ya. Frenkel. Publishing house “Chemistry”, M.-L., 1966.
[4] Konyukh I. V., Zabugina M. P., Vinogradov G. V. Factory laboratory. I, 123.1965.
[5] Tager A. A. Physicochemistry of Polymers, ed. Pth, ed. “Chemistry”, M. 1968.
[6] Vinogradov G. V., Prozorovskaya N. V. Plastic masses. 5, 50, 1964, 2, 36, 1966.
[7] Buniyat-zade A. A., Sagalaev G. V., Ismayilov T. M., Svyatodukhov B. P. Plastic masses, 12, 1972.
[8] Williams M. Z., Zandel R. F., Ferry J. D. J. Amer. Chem. Soc. 77, 3701, 1955.
[9] J. Ferry. Viscoelastic properties of polymers. Per. with English, ed. V. E. Gulya. Ed. IL, M., 1963.
[10] Tobolsky A. J. Polymer Sci Part C, 9, 157, 1965.
[11] Vinogradov G. V., Malkin A. Ya., Prozorovskaya N. V.
[12] Doolittle A. N., Appl Phys. 22, 1471, 1951, 23, 236, 1952, 28, 901.1957.
[13] Serenko O. A., Goncharuk G. P. et al. / Effect of temperature on the deformation behavior of a composite based on polypropylene and rubber particles // High Molecular Compounds.-2007.-No. 1.-P. 71-78.
[14] Derikov I. Ya., Kutergina I. Yu. et al. / Stable nonequilibrium composites based on liquid crystalline polymers and cadmium selenide nanoparticles // High Molecular Compounds. 2014. No. 4, pp. 408-418.
[15] Zaikin AE, Bobrov GB / Compatibilization of mixtures of incompatible polymers by filling // High-molecular compounds.-2012.-№8.-p. 1275-1282.
[16] Kuleznev V. N., Surikov P. V. // Phase equilibria in three-component polymer blends / High-molecular compounds.-2012.-No. 11.-p. 1602-1609.
[17] Chalykh A. E., Gerasimov V. K., Mikhailov Yu. M. Diagrams of the phase state of polymer systems. M.: Janus, 1998.
[18] Mulder M. // Basic Principles of Membrane Technology. Dordrecht: Kluwer, 1996.
[19] Belov N. A., Safronov A. P., Yu. P. Yampolsky // Reverse gas chromatography and thermodynamics of sorption in polymers. / High-molecular compounds.-2012.-No. 11.-p. 1631-1647.
[20] Bundjali B., Yudistira I., JAriah B, Sukria L. // Study on properties of Polymer Blends from Polypropylene with Polycaprolactone and their Biodegradability / Polymer Journal, -2007 - Vol. 39, No. 12.-pp. 1337-1344.
[21] Ermilova EA, Sizova AA, Ilyicheva NN, Pleshakov DV. // Investigation of the thermodynamic compatibility of a three-component mixture of nitramines with a copolymer of methyl methacrylate and methacrylic acid. / Advances in chemistry and chemical technology. 2014 - No. 2.-p. 65-67.
[22] Rijhikova I. G., Volkov A. M., et all. Modification feature of binary mixtures PP / SKEP by the system of organic peroxide-polyfunctional vinyl monomer in the reaction extrusion process. Plastic masses, 8, 2013, p. 40–45.
[23] Murtazina L. I., Garifullin A. R., Nikultsev I. A., et all. Influence of plastificators on the property of unhardened hermetics on the basis of ethylene-propylendiene rubber. Engineer-chemist’s encyclopedia, No. 8, 2014, pp. 31–35.
[24] Kirsh I. A., Pomogova D. A. Study of the properties of secondary polymer materials based on polypropylene and polyethyleneterephtalat, obtained in the influence of ultrasonic vibrations on the polymer melts. - Moscow, Plastic masses, 2012, No. 1, pp. 48-51.
[25] Kurbanova N. I. Heatelastolastics based on polypropylene and tri-etylene-propylene copolymer. Azerbaijan chemistry, - No. 1, - 2013, - P. 57–59. -2008 - No. 4.-p. 69-72.
[26] Turaev ER, Beknazarov Kh. S, Akhmedov UK, Jalilov AT. // Interphase interactions of three-phase polypropylene composite materials. / Universum. Technical sciences./- 2018-№12.- p. 57.
[27] Shastin D. A., Wolfson S. I., Makarov T. V.// Influence of modification of triple ethylene-propylene rubber on the physicomechanical properties of rubbers./ Vestnik of Kazan Technological University.-2010-№4.-p. 5-7.
[28] Ryzhikova I. G., Volkov A. M., Bauman N. A., Kazakov Yu. M., Wolfson S. I. // Influence of the concentration of components of the modifying system peroxide / TMPTA and the Mooney viscosity of rubber SKEPT on the balance of yield and impact resistance SKEPT master-batches in a polypropylene matrix. / Bulletin of the Technological University-2015-No. 4.-from 148-150.
[29] Ryzhikova I. G., Volkov A. M., Bauman N. A., Kazakov Yu. M., Wolfson C. B. - 2015. - No. 4.-p. 134-137.
[30] Nurmeeva EK. // Production and scope of ethylene-propylene rubbers SKEPT / Bulletin of Kazan Technological University.-2012-p. 129-131.
[31] Prospects for the development of production of ethylene-propylene rubber // Production and use of elastomers. - 1998. - No. 1. - S.53-54.
[32] Klyuchnikov I. O., Klyuchnikov O. R., Stoyanov O. V. // Bulletin of Kazan Technological University.
Cite This Article
  • APA Style

    Shixaliyev Kerem Sefi. (2019). Generalization of the Temperature Dependence of Some Physical Properties of High-strength Polyethylene (HDPE) Using the Method of Given Parameters. American Journal of Chemical Engineering, 7(6), 130-134. https://doi.org/10.11648/j.ajche.20190706.11

    Copy | Download

    ACS Style

    Shixaliyev Kerem Sefi. Generalization of the Temperature Dependence of Some Physical Properties of High-strength Polyethylene (HDPE) Using the Method of Given Parameters. Am. J. Chem. Eng. 2019, 7(6), 130-134. doi: 10.11648/j.ajche.20190706.11

    Copy | Download

    AMA Style

    Shixaliyev Kerem Sefi. Generalization of the Temperature Dependence of Some Physical Properties of High-strength Polyethylene (HDPE) Using the Method of Given Parameters. Am J Chem Eng. 2019;7(6):130-134. doi: 10.11648/j.ajche.20190706.11

    Copy | Download

  • @article{10.11648/j.ajche.20190706.11,
      author = {Shixaliyev Kerem Sefi},
      title = {Generalization of the Temperature Dependence of Some Physical Properties of High-strength Polyethylene (HDPE) Using the Method of Given Parameters},
      journal = {American Journal of Chemical Engineering},
      volume = {7},
      number = {6},
      pages = {130-134},
      doi = {10.11648/j.ajche.20190706.11},
      url = {https://doi.org/10.11648/j.ajche.20190706.11},
      eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.ajche.20190706.11},
      abstract = {In this paper, based on the study of HDPE by dilatometric and rheological methods in a wide range of temperatures and cooling and deformation rates, we generalized the temperature dependence of the physical properties of polyethylene using the specified parameters method. Test specimens (cylinder size: height 12 mm, diameter 9.3 mm) were obtained both in the dilatometer’s test cylinder itself and in a specially designed injection mold using injection molding on a TP-125 injection molding machineThe temperatures in the experiments were added and maintained with an accuracy of 3.2.°C. Defined by The dependence of ρ_0 T_0 / ρT (relative reduced density of the polymer) on the reduced temperature (T - T0). Test specimens (cylinder size: height 12 mm, diameter 9.3 mm) were obtained both in the dilatometer’s test cylinder itself and in a specially designed injection mold using injection molding on a TP-125 injection molding machine. It was found that a reliable characteristic of the dilatometric properties of the crystallizing polymer, physically correctly and completely reflecting the features of the crystalline structure, can be obtained only in the mode of stepwise temperature changes, when at each given temperature the equilibrium value of the specific sample of the primer is fixedThus, the practical value of the dilatometric method for studying crystallizing polymers is shown, especially when comparing the results of dilatometry with the results of rheological studies.},
     year = {2019}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - Generalization of the Temperature Dependence of Some Physical Properties of High-strength Polyethylene (HDPE) Using the Method of Given Parameters
    AU  - Shixaliyev Kerem Sefi
    Y1  - 2019/12/11
    PY  - 2019
    N1  - https://doi.org/10.11648/j.ajche.20190706.11
    DO  - 10.11648/j.ajche.20190706.11
    T2  - American Journal of Chemical Engineering
    JF  - American Journal of Chemical Engineering
    JO  - American Journal of Chemical Engineering
    SP  - 130
    EP  - 134
    PB  - Science Publishing Group
    SN  - 2330-8613
    UR  - https://doi.org/10.11648/j.ajche.20190706.11
    AB  - In this paper, based on the study of HDPE by dilatometric and rheological methods in a wide range of temperatures and cooling and deformation rates, we generalized the temperature dependence of the physical properties of polyethylene using the specified parameters method. Test specimens (cylinder size: height 12 mm, diameter 9.3 mm) were obtained both in the dilatometer’s test cylinder itself and in a specially designed injection mold using injection molding on a TP-125 injection molding machineThe temperatures in the experiments were added and maintained with an accuracy of 3.2.°C. Defined by The dependence of ρ_0 T_0 / ρT (relative reduced density of the polymer) on the reduced temperature (T - T0). Test specimens (cylinder size: height 12 mm, diameter 9.3 mm) were obtained both in the dilatometer’s test cylinder itself and in a specially designed injection mold using injection molding on a TP-125 injection molding machine. It was found that a reliable characteristic of the dilatometric properties of the crystallizing polymer, physically correctly and completely reflecting the features of the crystalline structure, can be obtained only in the mode of stepwise temperature changes, when at each given temperature the equilibrium value of the specific sample of the primer is fixedThus, the practical value of the dilatometric method for studying crystallizing polymers is shown, especially when comparing the results of dilatometry with the results of rheological studies.
    VL  - 7
    IS  - 6
    ER  - 

    Copy | Download

Author Information
  • The Department of “Organic Substances and Technology of Highmolecular Compounds”, Azerbaijan Oil and Industrial University, Baku, Azerbaijan

  • Sections